Grant Manufacturing & Alloying, Inc. |
DATA SHEET |
||
| Specification: ASTM B32-87 | 95Sn/5Sb Lead Free Solder | ||
| ELEMENT | SPECIFICATION | GMA TYPICAL ASSAY | |
| Tin (Sn) | 95.50 Max. - 94.50 Min. | 95.0% | |
| Antimony (Sb) | 5.25 Max. - 4.75 Min. | 5.0% | |
| Lead (Pb) | 0.01 Maximum | <0.01% | |
| Copper (Cu) | 0.08 Maximum | <0.008% | |
| Cadmium (Cd) | 0.001 Maximum | <0.001% | |
| Aluminum (Al) | 0.001 Maximum | <0.001% | |
| Bismuth (Bi) | 0.001 Maximum | <0.001% | |
| Arsenic (As) | 0.005 Maximum | <0.005% | |
| Iron (Fe) | 0.005 Maximum | <0.005% | |
| Zinc (Zn) | 0.005 Maximum | <0.005% | |
COMMON SIZES MANUFACTURED |
|||
| Bar / Ingot | 1 lb. to 50 lbs. | ||
| Anodes - Cast | Rectangle 1x4", "D" Shape 2"x4" | ||
| Anodes - Extruded | Star 16, 12 & 10 point, Oval 1.5"x3", Rectangle 1"x3", Square 1"x1" | ||
| Anodes - Basket | Flat Top 1.625" | ||
| Solidus Temperature | 450 F | ||
| Liquidus Temperature | 464 F | ||
| Pasty Range | 14 F | ||
| Tensile Strength - Cast | 5,900 psi | ||
| Tensile Strength - Soldered joint | 14,200 psi | ||
| Density | 0.260 lbs/cu in. | ||
| Electrical Conductivity | 11.9% IACS | ||
| Electrical Resistivity - at 77 F | 14.5 Microhm-cm | ||
| Shear Strength | 11,100 psi | ||
| Brinnel Hardness | 15 | ||